PVC sheath materials for wire and cable are a PVC-based pellet material which is produced by mixing and granulating with accessory ingredients such as plasticizers, fillers, stabilizers, lubricants and colorants.
1. Model, name and application of products
|
Model |
name |
application |
|
H-70 |
Support-level soft PVC plastic at 70 ℃ |
Sheath of wire and cable at 450/750V or below, Sheath of wire and cable at 26/35 V or below |
|
HR-70 |
Soft support-level soft PVC plastic at 70 ℃ |
Soft sheath of wire and cable at 450/750V or below |
|
HⅠ-90 |
Ⅰ type support-level soft PVC plastic at 90 ℃ |
Sheath of wire, cable and other similar cables at 35V or below |
|
HⅡ-90 |
Ⅱtype support-level soft PVC plastic at 90 ℃ |
Sheath of wire and cable at 450/750V or below |
|
H-105 |
PVC sheathing materials at 105 ℃ |
Sheath for wires and cables at temperature classification of 105 ℃ |
2. Executive Standard
GB/T 8815-2008、Q/WRD 001-2016
3. Products properties
The products properties are shown in Table 2.
4. Processing
Single screw extruder is used in processing, with the aspect ratio of screw L/D≥20. The recommended reference processing temperature is shown below:
|
Sections |
Section 1 |
Section 2 |
Section 3 |
Section 4 |
Extrusion head |
Die |
|
Temperature/℃ |
140±10 |
160±10 |
170±5 |
175±5 |
175±10 |
170±10 |
5. Packaging, transportation and storage
Package: net weight of each bag (25±0.2) kg. The inner bag is polyethylene film and the outer bag is craft paper composites.
Transportation and storage: no exposure to sunshine and rain during transportation. It should be stored in clean, cool, dry and ventilated warehouse.
Table 2 Products properties
|
Test items |
H-70 |
HR-70 |
HⅠ-90 |
HⅡ-90 |
H-105 |
|
Tensile strength/MPa ≥ |
|
|
|
|
|
|
Tensile strain at break/% ≥ |
|
|
|
|
|
|
Thermal deformation ≤ |
|
|
|
|
|
|
Impact brittle property |
Test temperature /℃ |
|
|
|
|
|
|
Impact brittle property |
Pass |
Pass |
Pass |
Pass |
Pass |
|
Thermal stabilization time at 200℃/min ≥ |
|
|
|
|
|
|
volume resistivity at 20℃/Ω·m ≥ |
|
|
|
|
|
|
dielectric strength /（MV/m）≥ |
|
|
|
|
|
|
dielectric loss factor(50Hz) ≤ |
|
|
|
|
|
|
volume resistivity at work temperature |
Test temperature /℃ |
|
|
|
|
|
|
volume resistivity/Ω·m ≥ |
|
|
|
|
|
|
Thermal aging test temperature/℃ |
|
|
|
|
|
|
Thermal aging test time/h |
|
|
|
|
|
|
Tensile strength after aging/MPa ≥ |
|
|
|
|
|
|
The biggest change rate of tensile strength/% |
|
|
|
|
|
|
Tensile strain at break after aging/% ≥ |
|
|
|
|
|
|
The biggest change rate of tensile strain at break/% |
|
|
|
|
|
|
Mass loss of thermal aging |
Test temperature/
℃ |
|
|
|
|
|
|
Test time/h |
|
|
|
|
|
|
Mass loss/(g/cm2) ≤ |
|
|
|
|
|